The effects of B addition on the magnetization, mechanical and shape memory properties in Cu70−xAl24Mn6Bx at.% (x = 0, 1, 2, 3, 4) alloys have been investigated. The ductility was decreased, while the strength was improved with B addition. Transformation temperatures were increased with B content due to increased e/a ratio. Martensite start temperature of B-free CuAlMn was found to be 37.3 °C and increased to 218.8 °C with 4 % B addition. B-free CuAlMn exhibited shape memory effect with a recoverable strain of 2.25 % under 200 MPa and a perfect superelasticity with a recoverable strain of 2.5 % at 163 °C. B addition degraded the shape memory properties and eventually resulted in the lack of recoverable strain. In addition, saturation magnetization was increased with B content. Moreover, the addition of B slightly decreased the ductility of the alloy. It was found that the magnetization, mechanical and shape memory properties CuAlMn alloys can be tailored by quaternary alloying with B. © 2016, Springer-Verlag Berlin Heidelberg.