Bayri, NevzatAtalay, Selçuk2024-08-042024-08-0420211307-90852149-4584https://doi.org/10.18185/erzifbed.722152https://search.trdizin.gov.tr/yayin/detay/478715https://hdl.handle.net/11616/88912In this study, the magnetoimpedance (MI) and stress impedance (SI) effect properties of Fe77.5Si7.5B15 wires have been investigated. Wires were annealed at 460 oC for different times. The largest change in the MI was observed at 1MHz ac current frequency value. At this frequency value, the change in MI was about 40% in the wire that as-received, while the change in the wire heat treated at 460 oC for 10 minutes was found to be 169%. It has been determined that low time annealed leads to increase in magnetic softness.eninfo:eu-repo/semantics/openAccessArticle141162610.18185/erzifbed.722152478715