Altin, SerdarYakinci, EyuphanBalci, YakupAksan, M. Ali2024-08-042024-08-0420051300-01011303-6122https://hdl.handle.net/11616/94220Bi-2212 superconducting single crystal (nano) whiskers have been fabricated by annealing a melt-quenched (glass) Bi3Sr2Ca2Cu3Ox precursor. A couple of (nano) Whiskers obtained were placed crosswise on a YSZ single crystal substrate and then heat treated at 830 C for 25 minute to form nano-scale junction. The T-c of each nano-whisker was found to be 85 K and the critical current density, J(c), of the whiskers was calculated to be 1177 Acm(-2) at zero field. The I - V characteristics of the nano-junction at 30 K were found to show a multiple-branch structure, which is the main behavior of the Josephson junction.eninfo:eu-repo/semantics/closedAccessBSCCO superconductorsHTc superconductorswhiskersArticle2953253282-s2.0-30444439091Q3WOS:000420222000007N/A