Yazar "Asiltürk, Meltem" seçeneğine göre listele
Listeleniyor 1 - 11 / 11
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Characterization of $TiO_2$ synthesized in alcohol by a sol-gel process: The effects of annealing temperature and acid catalyst(2005) Sayılkan, Funda; Asiltürk, Meltem; Sayılkan, Hikmet; Önal, Yunus; Akarsu, Murat; Arpaç, ErtuğrulThe effects of annealing temperature and hydrolysis catalyst on the crystalline form and crystallite size of $TiO_2$ prepared by a sol-gel process were investigated. Three types of $TiO_2$ were synthesized by hydrolysis of titanium(IV)-iso-propoxide with water in n-propanol without catalyst (Type-A) and with HCl as catalyst, where the $H^+/Ti^{4+}$ mol ratio was 0.54 for Type-B and 0.2 for Type-C. Hydrolysis products were thermally treated at 100, 200, 300, 400 and 500 °C for 1 h after drying at room temperature. Characterization of the particles was carried out using XRD, BET, TG/DTA and SEM analysis. The pore size distributions were computed by the DFT plus method. The results showed that the acid catalyst and catalyst/alkoxide ratio have a large effect on the formation of anatase $TiO_2$. In particular, it was found that anatase phase $TiO_2$ particles occur at 400 and 500 °C for Type-A $TiO_2$, while they do so at nearly 200 °C for Type-B and Type-C $TiO_2$. The crystallite size of Type-A, Type-B and Type-C increased from 17.96 to 19.24 nm, from 12.38 to 15.12 nm and from 10.60 to 12.20 nm, respectively, when the thermal treatment temperature was raised from 400 to 500 °C.Öğe Characterization of TiO_2 synthesized in alcohol by a sol-gel process: The effects of annealing temperature and acid catalyst(Turkish Journal of Chemistry, 2005) Sayılkan, Funda; Asiltürk, Meltem; Sayılkan, Hikmet; Önal, Yunus; Akarsu, Murat; Arpaç, ErtuğrulAbstract:The effects of annealing temperature and hydrolysis catalyst on the crystalline form and crystallite size of TiO2 prepared by a sol-gel process were investigated. Three types of TiO2 were synthesized by hydrolysis of titanium(IV)-iso-propoxide with water in n-propanol without catalyst (Type-A) and with HCl as catalyst, where the H+/Ti4+ mol ratio was 0.54 for Type-B and 0.2 for Type-C. Hydrolysis products were thermally treated at 100, 200, 300, 400 and 500 °C for 1 h after drying at room temperature. Characterization of the particles was carried out using XRD, BET, TG/DTA and SEM analysis. The pore size distributions were computed by the DFT plus method. The results showed that the acid catalyst and catalyst/alkoxide ratio have a large effect on the formation of anatase TiO2. In particular, it was found that anatase phase TiO2 particles occur at 400 and 500 °C for Type-A TiO2, while they do so at nearly 200 °C for Type-B and Type-C TiO2. The crystallite size of Type-A, Type-B and Type-C increased from 17.96 to 19.24 nm, from 12.38 to 15.12 nm and from 10.60 to 12.20 nm, respectively, when the thermal treatment temperature was raised from 400 to 500 °C.Öğe The effect of silane modification on the adsorptive properties of natural pyrophyllite and synthetic titanium-based powders prepared by the sol-gel process(Turkish Journal of Chemistry, 2005) Şener, Şadiye; Erdemoğlu, Murat; Asiltürk, Meltem; Sayılkan, HikmetAbstract: Our aim was to improve the relatively poor adsorption characteristics of natural pyrophyllite and those of TiOm and Ti(OR)x(OHy(O)z obtained from titanium tetraisopropoxide (TTIP) by the sol-gel process. For this purpose, the surfaces of the above-mentioned adsorbents were coated with a surface modifier by dipping them in 1% and 50% (w/w) solutions of N-(2-aminoethyl)-3-aminopropyltrimethoxysilane (DIAMO) in methanol. Realization of the coating processes was checked by FT-IR and SEM analyses. FT-IR analyses of the coated powders heat treated at 110 ?C showed that condensation took place between OH groups of prehydrolyzed silane molecules and hydroxyl groups and/or oxygen atoms on the surface of the powders, ensuring the attachment of the silane molecules to the surface. Adsorption properties of coated and uncoated adsorbents were compared. Adsorption percentage of natural pyrophyllite was 46.35% for 4-nitrophenol (4-NP) in aqueous solution, whereas 1% and 50% amino-coated pyrophyllite displayed 52.14% and 73.84% adsorption, respectively. The highest adsorption of 4-NP was realized when the calcinated powder obtained from the hydrolysis-condensation product of TTIP was coated with DIAMO from 50% solution.Öğe Hydrothermal synthesis, characterization and photocatalytic activity of nanosized TiO_2 based catalysts for rhodamine B degradation(Turkish Journal of Chemistry, 2007) Sayılkan, Funda; Asiltürk, Meltem; Şener, Şadiye; Erdemoğlu, Sema; Erdemoğlu, Murat; Sayılkan, HikmetHydrothermal synthesis, characterization and photocatalytic activity of nanosized TiO2 based catalysts for rhodamine B degradationÖğe Katyon veya anyon katkılanmış, nano tio2'in sentezi ve seçilmiş kirleticilerin fotokatalitik yıkımı zerine etkisinin araştırılması: Ortam Ara Ürünlerinin ve Toksik Etkilerinin Belirlenmesi(2014) Erdemoğlu, Sema; Özmen, Murat; Yesılada, Özfer; Asiltürk, Meltem; Güngördü, Abbas; Kiraz, Nadir; Özmen, Nesrin[Abstract Not Available]Öğe Katyon veya anyon katkılanmış, nano tio2'in zentezi ve seçilmiş organik kirleticilerin fotokatalitik yıkımı üzerine etkisinin araştırılması: Ortam ara ürünlerinin ve toksik etkilerinin belirlenmesi(2014) Erdemoğlu, Sema; Özmen, Nesrin; Kiraz, Nadir; Asiltürk, Meltem; Güngördü, Abbas; Özmen, Murat; Yesılada, Özfer[Abstract Not Available]Öğe Metal alkoksit temmeli kompozit materyal sentezi ve boya adsorpsiyonunda kullanımı(İnönü Üniversitesi, 2007) Asiltürk, Meltem[Abtsract Not Available]Öğe Nano metal oksit partiküllerinin sentezi ve yüksek kırılma indisine sahip ince kaplamaların hazırlanması(2011) Sayılkan, Funda; Asiltürk, Meltem; Kiraz, Nadir; Burunkaya, Esin[Abstract Not Available]Öğe A novel approach to the hydrothermal synthesis of anatase titania nanoparticles and the photocatalytic degradation of rhodamine B(Turkish Journal of Chemistry, 2006) Akarsu, Murat; Asiltürk, Meltem; Sayılkan, Funda; Kiraz, Nadir; Arpaç, Ertuğrul; Sayılkan, HikmetAbstract: A novel approach was developed for the synthesis of high-dispersed anatase nano-TiO2 by a hydrothermal process without solvent at 200 °C in 1 h. It was characterized using XRD, TEM, BET and elemental analysis. Nanoparticle-TiO2 was used as a photocatalyst by considering complete degradation of Rhodamine B (RB) dye. The photocatalytic reaction parameters such as photocatalyst amount, irradiation time and dye concentration were optimized and it was found that 0.125 wt% catalyst in 30 mg/L of RB aqueous solution is adequate for full degradation of RB in 50 min with 770 W/m2 irradiation power. Photocatalytic activity of the nanoparticle- TiO2 was compared with Degussa P-25 at optimum catalysis conditions determined for the nanoparticle- TiO2. It was concluded that when compared to Degussa P-25, the nanoparticle- TiO2 can be repeatedly used with increasing photocatalytic activity. The results revealed that the photodegradation of RB proceeds by pseudo first-order reaction kinetics in which the rate constant of the degradation is 0.132 min?1.Öğe Sucul Sistemlerde Nanomalzemelerin Çevresel Akibeti ve Ekotoksisitesinin Kestirimi(2017) Özmen, Murat; Asiltürk, Meltem; Güngördü, Abbas; Özmen, Nesrin; Erdemoğlu, SemaNanobilim ve nanoteknoloji ilaç geliştirme, su arıtımı, endüstriyel teknolojiler, daha dayanıklı ve daha hafif malzemeler üretilmesi gibi alanlarda önemli avantajlar sağlaması ve önemli potansiyellere sahip olması yönünden tüm dünyada çok hızlı gelişim gösteren alanlardır. Bununla birlikte, çevresel toksikantlar olarak rol oynaması ve kütlece büyük yapılı metallerlere (bulk) kıyaslandığında özellikle sucul organizmalarda daha fazla birikim riski bulunmasına karşın, nanoparçacıkların ekotoksikolojik riskleri hakkında bilinenler yeterli düzeyde değildir. Bazı nanoparçacıklar hücrede temel metabolik reaksiyonlara karışarak ve membrandan kolaylıkla geçerek toksik etkilere neden olabilir. Nanomalzemelerin kullanımındaki artışa ve fotokatalitik etkilerinin arttırılmasına karşın, toksik etkilerinin ve kullanım miktarlarının azaltılması çevre sağlığının korunması bakımından önem taşımaktadır. Dahası temiz ve güvenli su kaynakları insan ve çevre sağlığı bakımından esastır. Geleneksel fiziko-kimyasal yöntemler ile suların arıtılması birçok dezavantajlara sahip olduğundan, bu alanda nanomühendislik ürünü malzemeler dikkat çekmektedir. Bundan dolayı bu çalışmada yeni sentezlenmiş nano yapılı katkılanmış TiO2 parçacıkların ve çekirdek@kabuk yapılı nanoparçacıkların tatlısu organizmaları olan Danio rerio, Xenopus laevis, Daphnia magna ve Chlamydomonas reinhardtii ‘de toksik etkileri ayrı ayrı belirlenmiştir. Ayrıca sentezlenen nanoparçacıkların çevresel riskinin kestirimi amacıyla nanokozm modelleri geliştirilerek ekolojik risk tahminlerinde bulunulmuştur. Nanopartiküllerin seçilen çevresel kirlericilerin fotokatalitik yıkımına ve toksik etkisinin azaltılmasına etkileri değerlendirilmiştir. Bu amaçla bisfenol A (BPA; endokrin bozucu), fluoxastrobin (FLX; pestisit) ve dispers red 65 (DR65; azo boyası) seçilmiş olan çevresel kirleticilerdir. Araştırma sonuçlarına göre, sentezlenen nanoparçacıkların seçilen test organizmalarında düşük toksikolojik riske sahip olduğu, bununla birlikte D. magna’nın akut etkiye en duyarlı test organizması olduğu belirlenmiştir. D. rerio ve X. laevis embriyoları ve alg hücrelerinde sentezlenen nanoparçacıklar önemli bir toksik etki göstermemiştir. Diğer taraftan BPA ve DR65 boyar maddesinin sentezlenen yeni saf TiO2 ve SiO2@TiO2 nanoparçacıkları ile fotokatalitik yıkımı organizmaların embriyonik evresinde letal/toksik etkiyi önemli seviyede azaltmıştır. S- veya Mn- katkılanmış TiO2 ise BPA ve FLX pestisitinin toksik etkisinin azaltılmasında önemli rol oynamıştır. Çalışma sonuçları özgül nanoparçacıkların insan ve çevre sağlığının korunması için su kirliliğinin gideriminde kullanışlı olabileceğini göstermektedir. Bununla birlikte, nanoparçacıkların toksik etkisinin ekosistemin farklı trofik düzeylerinde değerlendirilmesi gerektiği de geşiltirilmiş olan basit nanokozm modelleri ile ortaya konulmuştur.Öğe Sulu çözeltide o-toludinin elektrokimyasal polimerizasyon parametlerinin incelenmesi(İnönü Üniversitesi, 2001) Asiltürk, Meltem[Abtsract Not Available]