    Determination of trace elements in kidneys, livers and brains of rats with sealer implants by ICP-MS
    (Taylor & Francis Ltd, 2017) Simsek, Neslihan; Akinci, Levent; Alan, Hilal; Gecor, Orhan; Ozan, Ulku
    Following root canal treatment, sealers may contact periapical tissue. The purpose of this study was to evaluate the systemic toxic effects of epoxy resin-based sealers (AH Plus and Obtuseal). Inductively coupled plasma-mass spectrometry (ICP-MS) was used to measure levels of trace elements (beryllium, magnesium, aluminium, calcium, chromium, arsenic and lead) in the brain, kidney and liver of rats. Twenty sterilized polyethylene tubes were then filled with AH Plus and Obtuseal and implanted into the dorsal subcutaneous tissue of 10 rats; three unoperated animals were used as a control group. After 45 days, the rats were sacrificed by cervical dislocation following anaesthesia, and brains, kidneys and livers were removed from all experimental animals. ICP-MS analysis was used to determine levels of trace elements. Data were analysed using Kruskal-Wallis and Connover post hoc tests. No significant differences were found in aluminium and calcium levels, but brains, kidneys and livers showed significantly higher amounts of magnesium and chromium than the corresponding controls. In the kidney and liver samples, arsenic levels were found to be higher than in the control group. Lead was detected at higher levels only in liver samples from the AH Plus group. Beryllium was not detected in any organ. It was concluded that AH Plus and Obtuseal release minimal quantities of trace elements when in contact with subcutaneous tissue, and further studies are needed to understand the systemic effects of these materials.
  • Küçük Resim Yok
    Öğe
    Effects of Local and Systemic Zoledronic Acid Application on Titanium Implant Osseointegration: An Experimental Study Conducted on Two Surface Types
    (Lippincott Williams & Wilkins, 2017) Dundar, Serkan; Yaman, Ferhan; Gecor, Orhan; Cakmak, Omer; Kirtay, Mustafa; Yildirim, Tuba Talo; Karaman, Tahir
    The aim of this study was to evaluate the effects of local and systemic zoledronic acid (ZA) applications on titaniumoksit ceramic blasted (TiO-CB)- and sandblasted large acid-grit (SLA)-surfaced titanium implant osseointegration. Twelve New Zealand White rabbits were used in the study, divided into 6 groups: the TiO-CB (TiO-CB-CNT) (n = 2) and SLA (SLA-CNT) (n = 2) control groups in which TiO-CB- and SLA-surfaced titanium implants were surgically inserted into rabbit tibias but no treatment was applied; the TiO-CB (TiO-CB-LZA) (n = 2) and SLA (SLA-LZA) (n = 2) local ZA groups in which 1 mL of normal saline solution containing 2 mg of ZA was injected into sockets and after this the implants were integrated; and the TiO-CB (TiO-CB-SZA) (n = 2) and SLA (SLA-SZA) (n = 2) systemic ZA groups in which a single infusion of 0.1 mg/kg of ZA was administered during surgical implant insertion. Following a period of osseointegration, bone implant contact (BIC) was recorded as a proportion of the total implant surface length in direct contact with the bone. Results of this study indicate that BIC was greater in the systemic ZA application groups than in the local ZA application groups, and BIC was greater in the local ZA groups than in the controls. Statistically significant differences in BIC were not detected between the TiO-CB- and SLA-surfaced implants in all the groups. Furthermore, this study did not reveal significant differences between the 2 types of surfaces due to similar average roughness values. Overall, systemic ZA application was found to be more effective in increasing BIC than local ZA application based on the results obtained by testing 2 implant surfaces.