Yazar "Uysal, Turan" seçeneğine göre listele
Listeleniyor 1 - 16 / 16
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Alumina Production from Clay Minerals: Current Reviews(Gazi Univ, 2018) Erdemoglu, Murat; Birinci, Mustafa; Uysal, TuranAlumina (Al2O3), which is a very important material due to its superior physical and technological properties, is widely used in industry and almost all of alumina is obtained from Bayer process using bauxite as a raw material. However, some technical and economical handicaps of alumina production with Bayer process (such as limited or non availability of bauxite reserves in some countries, reduction of high grade bauxite deposits, growing alumina demand for industry etc.) require alternative raw material sources and methods to produce alumina. Therefore, investigations on the alumina production from non-bauxite sources is one of the current studies in related literature as well. Clay minerals are considered to be the best available source of non-bauxite raw material for alumina production. Because clay minerals are abundant and common in the earth crust, they have relatively high grade of aluminum, when compared to other sources, clay mining is easier and require simpler preparation and enrichment processes. There are various processes developed to produce alumina from clays, but among them Acid Leaching Process has become well-known method that could be practiced as a more effective method in alumina production due to some advantages. Moreover, it is seen that there is a consensus on Acid Leaching Process. Besides, there are current studies investigating several technical modifications and improvements on the process steps. The aim of this study prepared by reviewing the studies obtained from literature and current experimental results on production of alumina from clays is to give information particularly to alumina industry and stakeholders and related researchers, and to contribute to scientific studies on this topic.Öğe Aluminum Recovery by Acid Leaching of Variously Enriched Pyrophyllite Ore: Effects of Pre-treatment Methods for Activation(Springer Heidelberg, 2023) Aydogmus, Ramazan; Erdemoglu, Murat; Uysal, TuranEffects of pre-treatment methods such as calcination for thermal activation and intensive milling for mechanical activation on the aluminum (Al) recovery by acid leaching of preliminarily enriched pyrophyllite ore via attrition scrubbing and froth flotation were investigated. XRD patterns of the calcined and the intensively milled samples were compared to determine the changes during the pre-treatment processes. Hot HCl solution was used for dissolution of aluminum to determine the Al recoveries from variously enriched and variously pre-treated pyrophyllite ore samples. Specific thermal and milling energies consumed per unit amount of ore were calculated, and the ideal activation method was suggested by comparing the activation methods in terms of energy consumption. Mechanical activation of the pyrophyllite concentrate obtained by attrition scrubbing rather than froth flotation was suggested for higher recoveries of aluminum from by acidic leaching. It was determined that operating cost (in terms of energy) of the mechanical activation is lower and aluminum recovery is higher than thermal activation. It was concluded that mechanical activation instead of thermal activation is more economical and environmentally friendly method.Öğe Contribution of Mechanical Activation for Obtaining Potassium Chloride from Microcline(Springer Heidelberg, 2023) Alyosif, Bahaa; Uysal, Turan; Aydemir, Muhammet Kuersat; Erdemoglu, MuratThe effect of intensive milling on the conversion of microcline (KAlSi3O8) to potassium chloride (KCl) occurred during the chlorination roasting process for artificial KCl production was investigated. A feldspar ore with 10.89% K2O grade and containing microcline was dry milled by a planetary ball mill for mechanical activation. Milled ore mixed with calcium chloride was roasted at temperatures between 500 and 1000 degrees C to get the chlorination roasting process. The product was then leached in water to dissolve KCl occurring during the roasting, which will be precipitated from the pregnant leach solution by evaporation. Results showed that potassium recovery from the unmilled ore increased rapidly up to 800 degrees C, and dramatically decreased at higher temperatures due to the removal of KCl from the furnace by means of evaporation. A potassium recovery of 31.95% was achieved by the unmilled ore, whereas it was 88.43% when 15 min milled ore was roasted at 750 degrees C. It was concluded that intensive milling caused mechanical activation of microcline to reduce the roasting temperature of the chlorination roasting process.Öğe Effects of mechanical activation of colemanite (Ca2B6O11•5H2O) on its thermal transformations(Elsevier, 2016) Uysal, Turan; Mutlu, H. Serdar; Erdemoglu, MuratIn this study, effects of mechanical activation on the thermal characteristics of colemanite (Ca2B6O11 center dot 5H(2)O) were examined with respect to its decrepitation behavior observed during the heating processes. Mechanical activation was achieved by milling (up to 150 min) in a planetary ball mill using tungsten carbide milling media. Crystallinity of the milled colemanite samples was determined by performing X-ray powder diffraction analysis. In this manner, milling conditions at which crystalline colemanite transforms to amorphous structure were obtained. Thermal gravimetric (TG) analyses together with differential thermal (DTA) and differential thermogravimetric (DTG) analysis were performed to determine how prolonged milling affects the thermal behavior of colemanite. It was found by examining the DTA data that intensive milling gives rise to removal of the crystal water from colemanite at low temperatures, which can be attributed to mechanical activation. DTG analysis revealed that mechanical activation decreases the rate of water removal from colemanite structure throughout the heating. It was suggested that mechanical activation eliminates the decrepitation almost completely, so that there is no need for pre-calcining operation which is generally required before manufacturing the colemanite-based high temperature materials. (C) 2016 Elsevier B.V. All rights reserved.Öğe EMPIRICAL INVESTIGATION OF TECHNOLOGY-INDUSTRY 4.0 RELATION OF THE EFFECT ON TRADE: AN ANALYSIS ON TURKEY(2019) Erdemoğlu, Murat; Birinci, Mustafa; Uysal, TuranÖz: Bu çalışmada, Pütürge (Malatya) pirofillit yatağından alınan %23,6 Al2 O3 içerikli cevherden asit liç işlemiyle alüminyum (Al) kazanımı üzerine aktivasyon koşullarının etkisi araştırılmıştır. Bu kapsamda, başlangıçta aktive edilmemiş tüvenan cevher ile daha sonra kalsinasyon ve aşırı öğütme yoluyla aktive edilmiş cevherler HCI ile liç edilmiştir. Elde edilen deneysel çalışma bulgularına göre; tüvenan, kalsine ve aşırı öğütülmüş cevher için liç çözeltisinde Al kazanımı sırasıyla %10,57, %33,63 ve %86,5 olarak bulunmuştur. Kalsinasyon işlemi sırasında kil tabakaları arasında yeterli bir açılmanın olmadığı ve gözenekli yapının elde edilemediği, ayrıca yüksek sıcaklıklarda asitte çözünmeye dirençli yeni mineral fazlarının ortaya çıktığı tespit edilmiştir. Bu nedenle termal yolla aktifleştirilmiş cevher için Al kazanımı nispeten düşük çıkmıştır. Öte yandan aşırı öğütmeyle sağlanan mekanik aktivasyonun cevherdeki kil minerallerinin amorflaşmasına yol açtığı, böylece alüminyumun çözeltiye geçme eğiliminde önemli bir iyileşme sağladığı görülmüştür. Sonuçta termal aktivasyonun kısmen, mekanik aktivasyonun ise çok belirgin bir şekilde Al kazanımını artırdığı sonucuna varılmıştır.Öğe Kil Minerallerinden Alümina Üretimi: Güncel Değerlendirmeler(Murat E., Mustafa B., Turan U. (2018). Kil Minerallerinden Alümina Üretimi: Güncel Değerlendirmeler, Politeknik Dergisi, İnönü Üniversitesi, Malatya., 2018) Erdemoğlu, Murat; Birinci, Mustafa; Uysal, TuranÖz: Günümüzde üstün fiziksel ve teknolojik özelliklerinden dolayı çok önemli bir malzeme olan alümina (Al2O3) endüstride yaygın bir şekilde kullanılmaktadır ve alümina üretiminin neredeyse tamamı hammadde kaynağı olarak boksitin kullanıldığı Bayer prosesi ile karşılanmaya devam etmektedir. Ancak yüksek üretim miktarlarına bağlı olarak Bayer prosesine beslenecek uygun kalitedeki boksit rezervlerinin hızla azalması, alümina üretim maliyetlerindeki artışlar, bazı ülkelerin boksit rezervlerinin sınırlı olması ya da hiç bulunmaması gibi teknik ve ekonomik gerekçelerden dolayı boksit dışı kaynaklardan alümina üretimi konusu hem bilimsel araştırma hem de endüstriyel uygulamalar açısından oldukça önem taşımaktadır. Doğada bol ve yaygın yaygın bir şekilde bulunmaları, nispeten yüksek alüminyum tenörüne sahip olmaları, madencilik yöntemleriyle üretimlerinin kolay ve ucuz olması, diğer kaynaklara göre daha basit hazırlama ve zenginleştirme işlemleri gerektirmeleri gibi nedenlerden dolayı kil mineralleri alümina üretimine en elverişli boksit dışı kaynak olarak görülmektedir. Killerden alümina üretimi amacıyla geliştirilmiş ve genel kabul görmüş bazı süreçler bulunmaktadır. Bunlar arasında özellikle “Asit Liç Süreci” daha fazla ön plana çıktığı, bazı üsünlüklerinden dolayı alümina üretiminde daha etkin bir yöntem olarak uygulanabileceği konusunda bir fikir birliği oluştuğu görülmektedir. Bununla birlikte süreç koşulları ve süreç işlem kademeleri üzerinde birtakım değişikliklere gidildiği, bazı modifikasyonların denendiği güncel çalışmalara rastlanılmaktadır. Killerden alümina üretimi konusunda yapılmış olan çalışmaların ve güncel araştırma bulgularının derlenmesiyle hazırlanan bu çalışmanın amacı, başta alümina endüstrisi ve paydaşları olmak üzere ilgili araştırmacılara bilgi vermek, bu alanda yapılan bilimsel çalışmalara katkı sunmaktır. Başlık (İngilizce): Alumina Production from Clay Minerals: Current Reviews Öz (İngilizce): Alumina (Al 2 O 3 ), which is a very important material due to its superior physical and technological properties, is widely used in industry and almost all of alumina is obtained from Bayer process using bauxite as a raw material. However, some technical and economical handicaps of alumina production with Bayer process (such as limited or non availability of bauxite reserves in some countries, reduction of high grade bauxite deposits, growing alumina demand for industry etc.) require alternative raw material sources and methods to produce alumina. Therefore, investigations on the alumina production from non-bauxite sources is one of the current studies in related literature as well. Clay minerals are considered to be the best available source of non-bauxite raw material for alumina production. Because clay minerals are abundant and common in the earth crust, they have relatively high grade of aluminum, when compared to other sources, clay mining is easier and require simpler preparation and enrichment processes. There are various processes developed to produce alumina from clays, but among them "Acid Leaching Process" has become well-known method that could be practiced as a more effective method in alumina production due to some advantages. Moreover, it is seen that there is a consensus on Acid Leaching Process. Besides, there are current studies investigating several technical modifications and improvements on the process steps.The aim of this study prepared by reviewing the studies obtained from literature and current experimental results on production of alümina from clays is to give information particularly to alumina industry and stakeholders and related researchers, and to contribute to scientific studies on this topic.Öğe Madencilik süreçlerinde membran teknolojileri ve uygulamaları(2021) Uysal, TuranMadencilikte membranlar, madencilik atıksularının arıtılması, atıksulardan değerli metal kazanımı, yüklü liç çözeltilerinin konsantrasyonu ve değerli metallerin kazanımı, Asit Maden Drenajı (AMD) arıtımı, asit, kostik ve siyanür geri kazanımı gibi farklı alanlarda kullanılmaktadır. Madencilikte membranlar, düşük maliyetli, kolay işletilebilir, çevreci, seçici, yüksek giderim verimi ve daha az yer kaplaması nedeniyle tercih edilmektedir. Bu çalışmada, madencilik endüstrisi tarafından Dünya’da ve ülkemizde kullanılmakta olan membran uygulamaları membran teknolojisindeki son gelişmeler ışığında değerlendirilmiştir. Bu değerlendirmelere göre yenilikçi membran proseslerinin gelişmesiyle membranların maliyet ve tıkanma sorunu gibi kritik özellikleri iyileştirilmiştir. Membran maliyetleri ve çalışma basınçları önemli oranda azalmış, tıkanma ve kirlenme sorunu kontrol edilebilir duruma gelmiştir. Böylece küresel ölçekte, madencilik endüstrisinde farklı amaçlarla membran kullanımı yaygınlaşmış ve ideal bir yöntem haline gelmiştir. Ülkemizde ise devam eden çalışmalarla birlikte yakın zamanda bu teknolojinin madencilikte yaygınlaşacağı öngörülmektedir.Öğe Mechanical activation of pyrophyllite ore for aluminum extraction by acidic leaching(Springer, 2018) Erdemoglu, Murat; Birinci, Mustafa; Uysal, Turan; Tuzer, Esra Porgali; Barry, Thierno SaidouA pyrophyllite [Al2Si4O10(OH)(2)] ore as an alternative source for alumina (Al2O3) was intensively milled for mechanical activation to increase aluminum extraction by acid leaching method. For this purpose, unmilled and milled ore samples were compared to reveal the changes caused by intensive milling. The samples were also leached in HCl solutions to determine whether mechanical activation increased the alumina extraction or not. The milling considerably disrupted XRD peak intensities of the clay minerals found in the ore, except quartz. After milling just for 30 min, peaks of the minerals were not distinguished, suggesting that all are amorphous. Dehydroxylation of the minerals in the unmilled ore was realized to occur at lower temperature ranges and energy consumed for dehydroxylation significantly reduced with prolonged milling. While aluminum recovery by leaching of the unmilled ore was about 12%, it increased to 73.09% as a result of milling the ore for 50 min. It was concluded that as the milling time is extended, energy needed to undergo dehydroxylation due to amorphization continues to decrease and aluminum recovery reaches higher values, suggesting that the clay minerals in the ore can be converted to mechanically activated state.Öğe Pirofillit Cevherinden Alümina Üretimine Zenginleştirme Yöntemlerinin Etkisi(2023) Aydoğmuş, Ramazan; Uysal, Turan; Erdemoğlu, MuratBu çalışmada, pirofillit cevherinden alüminyum (Al) kazanımı üzerine farklı zenginleştirme yöntemlerinin etkisi araştırılmıştır. Zenginleştirme yöntemleri pirofillitin doğal hidrofob yapısından dolayı flotasyon yöntemi, kırılganlık farklılığından dolayı ise Aşındırmalı Yıkama (AY) yöntemi kullanılmıştır. Zenginleştirme sonucu konsantre numunelere HCl ile liç işlemi yapılmış, liç sonucu çözeltiye geçen Al miktarları karşılaştırılarak değerlendirilmiştir. Pirofillit cevherinin AY yöntemi ile zenginleştirilmesi sonucu %54.79 verimle %27.44 Al2O3 tenörlü bir konsantre, flotasyon yöntemi ile ise %30.49 verimle %28.05 Al2O3 tenörlü bir konsantre elde edilmiştir. Buna göre zenginleştirme verimi açısından AY yöntemi daha verimli iken liç verimi açısından ise flotasyon yönteminin daha verimli olduğu belirlenmiştir. Tüvenan cevhere göre nihai alümina miktarı ve saflığı birlikte değerlendirildiğinde doğrudan liç ve AY konsantresi değerlerinin birbirine yakın olduğu belirlenmiştir. Sonuç olarak pirofillit cevherinden alümina üretimi için ayrıntılı ekonomik analiz yapılarak uygun yöntemin belirlenmesinin daha doğru olacağı değerlendirilmektedir.Öğe Pirofillit Cevherinden Alüminyum Titanat Üretimi(2022) Uysal, Turan; Erdemoğlu, MuratAlüminyum titanat (Al2TiO5), alümina (Al2O3) ve titanyum oksit (TiO2) bileşenlerinden yapay olarak üretilen ileri seramik bir malzemedir. Bu çalışmada alüminyum titanat üretmek için pirofillit cevherinden üretilen alümina ve ticari rutil kullanılmıştır. Çalışmada kullanılan alümina, pirofillit cevherinin HCl liçi ile elde edilen yüklü çözeltiden çöktürülen alüminyum klorür tuzunun kavrulması sonucu elde edilmiştir. Elde edilen alümina ve ticari rutil karışımı alüminyum titanat üretmek amacıyla aşırı öğütülmüş, şekillendirilmiş ve farklı sıcaklıklarda sinterlenmiştir. Sinterleme sonucu alüminyum titanat oluşumu öğütülmüş karışımda 1359 °C iken öğütülmemiş karışımda 1367 °C’dir. Aşırı öğütülmüş karışımdan daha düşük sıcaklıkta alüminyum titanat oluşması, mikroçatlak ve gözenekliliğin daha az olması mekanik aktivasyonun etkisini açıkça göstermektedir. Sonuç olarak pirofillit cevherinden hidrometalurjik süreçlerle kazanılan alüminadan, katma değeri daha yüksek olan alüminyum titanat üretilebileceği belirlenmiştir.Öğe PİROFİLLİT CEVHERİNDEN ASİT LİÇİ YÖNTEMİYLE ALÜMİNYUM KAZANIMINA AKTİVASYONUN ETKİSİ(Bilimsel Madencilik Dergisi, 2019) Uysal, Turan; Erdemoğlu, Murat; Birinci, MustafaÖz: Bu çalışmada, Pütürge (Malatya) pirofillit yatağından alınan %23,6 Al2 O3 içerikli cevherden asit liç işlemiyle alüminyum (Al) kazanımı üzerine aktivasyon koşullarının etkisi araştırılmıştır. Bu kapsamda, başlangıçta aktive edilmemiş tüvenan cevher ile daha sonra kalsinasyon ve aşırı öğütme yoluyla aktive edilmiş cevherler HCI ile liç edilmiştir. Elde edilen deneysel çalışma bulgularına göre; tüvenan, kalsine ve aşırı öğütülmüş cevher için liç çözeltisinde Al kazanımı sırasıyla %10,57, %33,63 ve %86,5 olarak bulunmuştur. Kalsinasyon işlemi sırasında kil tabakaları arasında yeterli bir açılmanın olmadığı ve gözenekli yapının elde edilemediği, ayrıca yüksek sıcaklıklarda asitte çözünmeye dirençli yeni mineral fazlarının ortaya çıktığı tespit edilmiştir. Bu nedenle termal yolla aktifleştirilmiş cevher için Al kazanımı nispeten düşük çıkmıştır. Öte yandan aşırı öğütmeyle sağlanan mekanik aktivasyonun cevherdeki kil minerallerinin amorflaşmasına yol açtığı, böylece alüminyumun çözeltiye geçme eğiliminde önemli bir iyileşme sağladığı görülmüştür. Sonuçta termal aktivasyonun kısmen, mekanik aktivasyonun ise çok belirgin bir şekilde Al kazanımını artırdığı sonucuna varılmıştır. Başlık (İngilizce): EFFECT OF ACTIVATION ON ALUMINUM RECOVERY FROM PYROPHYLLITE ORE BY ACID LEACHING Öz (İngilizce): In this study, effect of activation conditions on the recovery of aluminum (Al) obtained by acid leaching from Pütürge (Malatya) pyrophyllite ore containing 23.6% Al2 O3 was investigated. In this context, the initially non-activated ore and later activated ore samples using calcining and intensive milling were leached with HCl, separately. According to the experimental results, Al-recovery in the leachate for the raw, calcined and intensively milled ore samples were found to be 10.57%, 33.63% and 86.5%, respectively. It was also found that there was not sufficient dilation between the clay layers during calcination and the porous structure could not be obtained, also the new mineral phases which resist to dissolution in acidic media were formed at high temperatures. For this reason, the aluminum recovery of thermally activated ore was relatively low. However, it was confirmed that mechanical activation by intensive milling led to amorphization of clay minerals, and thus, the mechanical activation significantly improved the dissolution behavior of aluminum. As a result of this study, it is concluded that while Al recovery is slightly increased by thermal activation, it is dramatically increased by mechanical activation.Öğe Production of Aluminum Titanate from Pyrophyllite Ore(Gazi Univ, 2022) Uysal, Turan; Erdemoglu, MuratAluminum titanate (Al2TiO5) is an advanced ceramic material produced artificially from the alumina (Al2O3) and titanium oxide (TiO2) components. In this study, alumina which is produced from pyrophyllite ore and commercial rutile were used to manufacture the aluminum titanate. The alumina used in the study was obtained by roasting the aluminum chloride salt precipitated from the loaded solution obtained by HCl leaching of the pyrophyllite ore. The resulting alumina and commercial rutile mixture is intensively milled, shaped and sintered at different temperatures to produce aluminum titanate. The result of sintering is that aluminum titanate formation is at 1359 degrees C in the milled mixture and at 1367 degrees C in the unmilled mixture. Formation of aluminum titanate at a lower temperature than the unmilled mixture, much less presence of microcracks and lack of pores clearly demonstrate the effect of mechanical activation. As a result, it has been shown that aluminum titanate with high added value can be produced from alumina recovered from pyrophyllite ore by hydrometallurgical processes.Öğe Removal of heavy metal ions from aqueous medium using Kuluncak (Malatya) vermiculites and effect of precipitation on removal(Elsevier, 2014) Sis, Hikmet; Uysal, TuranThe removal of heavy metal ions, Cr3+, Pb2+ and Zn2+, by vermiculite was studied by batch adsorption tests. Influence of experimental parameters (e.g., medium pH and initial ion concentration) on removal was examined separately. Metal hydroxide formation in the dispersions and their precipitation was also investigated to assess the effect of precipitation on ion removal. For this purpose, some removal tests were carried out in the absence of vermiculite at various pH and initial ion concentrations. Electrokinetic and other properties (e.g., specific surface area, thermal and chemical analysis) of vermiculite were determined to explain the experimental results and the interaction mechanisms between solid surface and the ions. Zeta potential data were found to be a very useful means to explain the interaction mechanism between the adsorbent and adsorbate. The affinity of vermiculite for ions changed in the order of Pb>Cr>Zn. At the lowest studied pH of 2.5, 15.81, 10.71 and 9.18 mg of Pb, Cr and Zn ions could be removed by 1 g of the adsorbent, respectively. (C) 2014 Elsevier B.V. All rights reserved.Öğe Su içerisindeki ağır metal iyonlarının kuluncak (Malatya) vermikülitleri üzerine adsorpsiyonu(İnönü Üniversitesi, 2012) Uysal, TuranAdsorpsiyon uygulamalarındaki ucuz sorbent arayışı, kil minerallerinin ağır metal iyonlarını tutabilme özelliğinin araştırılmasına neden olmaktadır. Bu çalışmada, atık sulardaki Zn2+, Pb2+ ve Cr3+ iyonlarının Kuluncak (Malatya) vermikülitleri üzerine adsorpsiyon mekanizması belirlenmiştir. Bu amaçla, değişik koşullarda kesikli adsorpsiyon deneyleri yapılmış olup, optimum proses parametreleri belirlenmiştir. Elde edilen veriler bilinen adsorpsiyon modellerine uyarlanmıştır. Zn+2, Pb+2 ve Cr+3 iyonlarının vermikülit ile gideriminde; adsorban dozajı, karıştırma süresi, metal iyon derişimi, pH, gibi parametrelerin etkileri araştırılmıştır. Ayrıca çökelmenin adsorpsiyon ve metal iyon giderimi üzerine etkisi incelenmiştir. Bu ağır metal iyonlarının vermikülit ile giderimi için izoterm çalışmaları yapılmış ve elde edilen adsorpsiyon verilerinin Langmuir izoterm modeline uyduğu belirlenmiştir. Deneysel çalışmalar sonucunda 100 mL toplam çözeltideki optimum adsorban miktarı 1 g, karıştırma süresi 2 saat ve pH; çinko için pH 7, kurşun ve krom için ise pH 5,5 olarak belirlenmiştir. Buna göre maksimum adsorplama kapasitesi; çinko için 15,32 mg/g, kurşun için 29,59 mg/g ve krom için ise 27,70 mg/g olarak bulunmuştur. Sonuç olarak optimum şartlar sağlandıktan sonra vermikülit minerali diğer adsorbanlarla karşılaştırıldığında, Kuluncak vermikülitlerinin adsorban olarak kullanılabileceği tespit edilmiştir.Öğe Thermal and Mechanical Activation in Acid Leaching Processes of Non-bauxite Ores Available for Alumina Production-A Review(Springer Heidelberg, 2019) Barry, Thierno Saidou; Uysal, Turan; Birinci, Mustafa; Erdemoglu, MuratThe rapid development of the global alumina and aluminum industry is straight coupled with the demands and the needs of these materials. Nowadays, the only well-known accessible resources to produce alumina and aluminum are bauxite ores. But bauxite ores are limited, and the remaining exploitable reserves do not have high contents in alumina. In countries where there is little or no bauxite reserves or where the recovery of existing bauxite ores to produce alumina with the Bayer process are not economic, alternative resources for alumina have been explored. The most attractive resources for replacing bauxites are aluminosilicate clay minerals and coal fly ash. The important processes developed for the recovery of alumina from these sources are acid leaching and alkaline leaching processes. The acid leaching is known as the most efficient in which thermal and mechanical activation are included for improving the performance of the process. The objective of this review is to give a comprehensive insight on the production of the alumina from thermally or mechanically activated clays and coal fly ash by hydrochloric, sulfuric, and nitric acid leaching processes.Öğe Thermal Behavior of Pyrophyllite Ore during Calcination for Thermal Activation for Aluminum Extraction by Acid Leaching(Springer, 2020) Erdemoglu, Murat; Birinci, Mustaea; Uysal, TuranIn the production of alumina (Al2O3) from clays by acid leaching, thermal activation by calcination is applied widely as a pre-treatment to improve the dissolution of aluminum. Previous studies have focused only on the thermal behavior of high-purity kaolinite and pyrophyllite, individually. However, thermal activation of complex clay ores containing several silicate minerals and their effect on aluminum extraction have not been studied. The purpose of the present study was to characterize the thermal behavior of a clay ore containing mainly pyrophyllite (Al2Si4O10(OH)(2)), kaolinite (Al2Si2O5(OH)(4)), muscovite (KAl2(AlSi3O10)(OH)(2)), quartz (SiO2), and kyanite (Al2SiO5) from the Puturge clay deposits (Malatya, Turkey) for possible use in alumina (Al2O3) production by acid leaching. The ore and its calcination products obtained at various temperatures were characterized with respect to their mineral paragenesis, crystal structure, surface morphology, and thermal, calorimetric, and aluminum dissolution properties in order to understand the changes that occurred. Aluminum recovery in the leach solution increased in direct proportion to the dehydroxylation degree (D-tg) of the ore as the calcination temperature increased to 900 degrees C. A maximum aluminum extraction of 90.57% was achieved by leaching of the product from calcination at 900 degrees C. Aluminum extraction decreased sharply above that temperature, even though D-tg increased a little. By increasing the calcination temperature; the structures of pyrophyllite, kaolinite, and muscovite were destroyed by dehydroxylation, resulting in the exfoliation of the mineral layers, thus, a mixture of dehydroxylated phases formed. Depending mainly on the temperature range at which each of the dehydroxylated phases is durable, aluminum could be leached to some extent. The sharp decrease in the extraction of aluminum, iron, and potassium at higher temperatures was attributed to compaction of previously exfoliated layers of the minerals through re-crystallization to form mullite-like structures which seemed insensitive to acid attack during the leaching.