The effect of Sn content on mechanical, magnetization and shape memory behavior in NiMnSn alloys
Küçük Resim Yok
Tarih
2016
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Sa
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The effects of the composition alteration on the magnetization and shape memory behavior of Ni50Mn40-xSn10+x (x = 0, 1, 2, 3) alloys were systematically investigated by thermal, magnetic and mechanical experiments. Phase transformation from ferromagnetic austenite to weakly magnetic martensite was observed during thermal cycling under magnetic field and transformation temperatures were decreased with increasing Sn (or decreasing Mn). Moreover, the saturation magnetization of martensite increased with Sn content. Ni50Mn40Sn10 showed the recoverable strain of 2.1% during thermal cycling under 300 MPa and the reversible superelastic strain of 2% at 190 degrees C. Mechanical experiments exhibited that the largest compressive deformation of about 7% at 650 MPa occurred in Ni50Mn39Sn11 while Ni50Mn40Sn10 had fractured at 4% and 390 MPa at room temperature. (C) 2016 Elsevier B.V. All rights reserved.
Açıklama
Anahtar Kelimeler
Shape memory, Composition alteration, Superelasticity, Phase transformation, Saturation magnetization
Kaynak
Journal of Alloys and Compounds
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
683