Magnetic and Magnetoelastic Properties of Annealed Cold-Drawn CoSiB Amorphous Wires

Basit Öğe Kaydı
dc.authoridBayri, Nevzat/0000-0001-7105-7707
dc.authoridKolat, Veli Serkan/0000-0002-8864-5051;
dc.authorwosidBayri, Nevzat/ABG-9663-2020
dc.authorwosidKolat, Veli Serkan/ABI-5280-2020
dc.authorwosidIzgi, tekin/ABH-5655-2020
dc.authorwosidAtalay, Selcuk/AAA-5095-2021
dc.contributor.authorAtalay, S.
dc.contributor.authorBayri, N.
dc.contributor.authorKolat, V. S.
dc.contributor.authorIzgi, T.
dc.date.accessioned2024-08-04T20:41:08Z
dc.date.available2024-08-04T20:41:08Z
dc.date.issued2015
dc.departmentİnönü Üniversitesien_US
dc.description.abstractThe dependence of the magnetisation loops, coercivity, anisotropy constant and Delta E effect (the change of Young's modulus as a function of the magnetic field) was studied in negatively magnetostrictive Co Si-72.5 (12.5) B (15) cold-drawn amorphous wires, with a mean diameter of 100 A mu m, under annealing conditions. Samples were annealed at a temperature of 460 C-a similar to for time periods between 0.3 and 1300 min. The results indicated that progressive annealing initially led to relief of the internal stresses and that annealing of the wire at 460 C-a similar to for 90 min produced the minimum coercivity, which was similar to 0.0063 Oe. Further annealing increased the coercivity and anisotropy due to partial crystallisation at the surface. The maximum change in Young's modulus was similar to 27 % and was seen in the wire that was annealed for 60 min.en_US
dc.description.sponsorshipInonu University [2012/37]en_US
dc.description.sponsorshipThis work was supported by Inonu University with project number 2012/37.en_US
dc.identifier.doi10.1007/s10948-014-2925-1
dc.identifier.endpage1628en_US
dc.identifier.issn1557-1939
dc.identifier.issn1557-1947
dc.identifier.issue5en_US
dc.identifier.scopus2-s2.0-84939979089en_US
dc.identifier.scopusqualityQ3en_US
dc.identifier.startpage1621en_US
dc.identifier.urihttps://doi.org/10.1007/s10948-014-2925-1
dc.identifier.urihttps://hdl.handle.net/11616/96944
dc.identifier.volume28en_US
dc.identifier.wosWOS:000352619700028en_US
dc.identifier.wosqualityQ3en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.language.isoenen_US
dc.publisherSpringeren_US
dc.relation.ispartofJournal of Superconductivity and Novel Magnetismen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectYoung's modulusen_US
dc.subjectAmorphous wiresen_US
dc.subjectMagnetisation loopen_US
dc.titleMagnetic and Magnetoelastic Properties of Annealed Cold-Drawn CoSiB Amorphous Wiresen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu