Giant stress-impedance effect in Fe71Cr7Si9B13 amorphous wires
Küçük Resim Yok
Tarih
2004
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Sa
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The giant stress-impedance (SI) effect in as-received and furnace annealed Fe71Cr7Si9B13 amorphous wires is studied. Samples were annealed at temperature of 460degreesC for times between 0.3 and 300 min to remove internal stresses. The results show that the magnetoimpedance and SI effect change sharply with annealing and a maximum stress-impedance ratio of 255% is observed in the wire annealed for 10 min under an applied tensile stress of 250 MPa. (C) 2004 Elsevier B.V. All rights reserved.
Açıklama
Anahtar Kelimeler
amorphous materials, magnetoimpedance, stress-impedance