Effect of tensile stress on magnetoimpedance properties of CoNiFe/Cu wire
Küçük Resim Yok
Tarih
2009
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Iop Publishing Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
A Co20.5Ni40.5Fe39 magnetic film was electrodeposited onto a copper wire 50 mu m in diameter. The magnetoimpedance (MI) effect, (Delta Z/Z)(H)(%) = ((Z(H)-Z(max))/Z(max)) x 100, was measured in the Co20.5Ni40.5Fe39/Cu composite wire under varying tensile stresses up to 30 MPa. The results showed that large MI and stress impedance (SI) effects can be observed in the Co20.5Ni40.5Fe39/Cu composite wire. The MI curve at zero tensile stress shows a small split peak in the low-field region. With increasing applied tensile stress, single-peak behaviour of the MI effect is observed. The magnitude of the MI and SI effects decreases with increasing tensile stress, sigma. The peak values of (Delta Z/Z)(H)(%) for the sample decrease from 265% at sigma = 0 to 39% at sigma = 30MPa at 40 kHz ac driving-current frequency. The impedance of a sample under the effect of 25 MPa tensile stress at 40 kHz ac driving-current frequency showed variations of about 146%. It was also found that the frequency value, f*, where the maximum MI effect was observed as a function of driving-current frequency, increases with increasing tensile stress.
Açıklama
Anahtar Kelimeler
Giant Magneto-Impedance, Nife/Cu Composite Wires, Amorphous Wires, Plated Wire, Current-Density, Fe-Rich, Microwires, Anisotropy, Field, Microtubes
Kaynak
Journal of Physics D-Applied Physics
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
42
Sayı
17