Fabrication of Novel Geopolymer Grout as Repairing Material for Application in Damaged RC Beams
Küçük Resim Yok
Tarih
2022
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer Int Publ Ag
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, a new grouting composite, called geopolymer grout, with high compressive strength (> 107 MPa, cured at ambient conditions) was developed and injected into damaged reinforced concrete (RC) beam. This investigation was planned in two steps: (1) determination of optimum geopolymer grout composite depending on viscosity, compressive strength, and SEM findings; (2) injection of optimum geopolymer grout to damaged RC beam. Geopolymer grouts were fabricated with different NaOH concentrations (i.e., 8, 10, and 12 M) and Ca(OH)(2) contents (1, 3, 5 and 7% of slag weight). A remarkable advance in fresh and hardened characteristics of geopolymer grouts was acquired with changing of NaOH concentration and Ca(OH)(2) content. A reference RC beam was subjected to bending test and the load-displacement curve was obtained. The determined optimum geopolymer grout was injected into this damaged RC beam and exposed to reloading test. The strengthened RC beam specimen was compared with reference RC beam in terms of failure modes, load capacity and crack patterns. After damaged RC beam was strengthened, it showed higher mechanical performance compared to reference RC beam. The experimental findings revealed that geopolymer grouts could be a suitable alternative for repair and strengthening of damaged RC beam due to their low viscosity, eco-friendliness, good bonding and superior compressive strength.
Açıklama
Anahtar Kelimeler
Geopolymer grout, NaOH concentration, Ca(OH)(2) content, RC beam, Strengthening
Kaynak
International Journal of Civil Engineering
WoS Q Değeri
Q3
Scopus Q Değeri
Q2
Cilt
20
Sayı
4