Development of the hardness, three-point bending, and wear behavior of self-lubricating Cu-5Gr/Al2O3-Cr3C2 hybrid composites
Küçük Resim Yok
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Sage Publications Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This research aims to assess the mechanical characteristics of high-performance copper composites made utilizing powder metallurgy. The composites were produced by adding reinforcement elements (Al2O3-Cr3C2) at different rates (3-6-9 wt.%) into copper-graphite (Cu-5Gr) via hot pressing technique. The microstructure, hardness, three-point bending and wear performance were analysed. The results determined that hybrid reinforced composites exhibited higher density, hardness and bending strength compared to Cu-Gr composites. The highest hardness of 73.02 HB was found in the CG-4 (copper graphit-4) sample. The maximum bending stress of 151.06 MPa occurred in sample CG-2. In addition, it was observed that the wear resistance increased significantly with the addition of the hybrid reinforcements. The lowest specific wear rate of 7.961 x 10(-7) mm(3)/N.m occurred in sample CG-6. As a result, 15.92%, 58.16% and 83.21% improvements were achieved in hardness, bending strength and wear performance, respectively. The current work indicates that certain mechanical properties of copper can be improved via the powder metallurgy process and the addition of reinforcements which could expand the applications and use of this metal in different industries.
Açıklama
Anahtar Kelimeler
Copper, Graphite, Self-lubricating, Specific wear rate, Friction
Kaynak
Journal of Composite Materials
WoS Q Değeri
Q3
Scopus Q Değeri
Q2
Cilt
57
Sayı
8