Effects of In-situ and Ex-situ Heat-Treatment Procedures on the Transport Properties of the MgB2 Superconducting Thin Films Fabricated by Ultrasonic Spray Pyrolysis (USP) System
Küçük Resim Yok
Tarih
2011
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Superconducting MgB2 thin films have been prepared using Ultrasonic Spray Pyrolysis (USP) system. 2.4 MHz USP system and various solutions which contain different Mg, B and de-ionized water and LAPSA concentrations and gas atmospheres were used to obtain 500 nm to 1.0 mu m thick MgB2 films. Some of the films produced were heat treated in-situ in the spraying chamber during deposition and some of them were annealed ex-situ in the tube furnace under Mg vapor. T (c) and T (zero) of the samples were obtained to be 39.5 K and 37.4, 39.5 and 37.0 for ex-situ and in-situ prepared films, respectively. The highest critical current density was obtained to be 4.12x10(6) A cm(-2) for ex-situ annealed films and 4.01x10(6) A cm(-2) for in-situ produced films. The result obtained indicated that the ex-situ preparation method provides improvement in the transport and magnetic properties.
Açıklama
Anahtar Kelimeler
MgB2 superconductor, Ultrasonic spray pyrolysis, Nano-sized spherical MgB2 powders, Superconducting MgB2 powders
Kaynak
Journal of Superconductivity and Novel Magnetism
WoS Q Değeri
Q4
Scopus Q Değeri
N/A
Cilt
24
Sayı
1-2