Magnetotransport and magnetoresistance properties of Pr 0.68Ca0.32-xSrxMnO3 (x= 0, 0.1, 0.18, 0.26 and 0.32) manganites
Küçük Resim Yok
Tarih
2011
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
National Institute of Optoelectronics
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, the magnetotransport and magnetoresistance properties of Pr0.68Ca0.32-xSrxMnO3 (x= 0, 0.1, 0.18, 0.26 and 0.32) compounds were investigated. The system illustrate an evolution from a charge-ordered manganite at x = 0, with an insulating-like resistivity and low magnetization values, towards to a completely ferromagnetic metallic state for x = 0.32. Above the metal-insulator transition temperature TMI, the resistance curves were fitted to the small polaron popping model. The activation energy (Ea) was found to decrease with increasing Sr content. In the phase separated (PS) state, due to the coexistence of ferromagnetic (FM) metallic and charge order (CO) insulating phases, the magnetoresistance (MR) was found to be maximum. The MR ratio of 6.3x10 8 for the sample x = 0 at 60 K is one of the largest MR change has been reported in manganites. The MR values decreases considerably with increasing Sr content and the activation energy decreases with the increase of Sr content.
Açıklama
Anahtar Kelimeler
Colossal magnetoresistance, Manganites, Metal-insulator transition, Transport and magnetic properties
Kaynak
Journal of Optoelectronics and Advanced Materials
WoS Q Değeri
Scopus Q Değeri
Q4
Cilt
13
Sayı
6