Magnetoimpedance effects in a CoNiFe nanowire array
Küçük Resim Yok
Tarih
2013
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Sa
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This report describes the growth of CoNiFe nanowires into highly ordered porous anodic alumina oxide (AAO) templates by DC electrodeposition at a pH value of 2.6. Scanning electron microscopy (SEM) observations revealed that the wires have diameters of approximately 270-290 nm and a length of 25 mu m. The energy dispersive X-ray (EDX) analysis indicated that the composition of the nanowires is Co12Ni64Fe24. Electrical contacts were created on both sides of the nanowire array, and their magnetoimpedance (MI) properties were investigated. The impedance value was initially 1.2 ohm at low frequency and increased to approximately 1000 ohm for a 33-MHz driving current frequency under no applied magnetic field. All the MI curves exhibited single peak behaviour due to the high shape anisotropy. The maximum MI change at the 33-MHz driving current frequency was 2.72%. The maximum resistance change was 5.4% at 33 MHz. (C) 2013 Elsevier B. V. All rights reserved.
Açıklama
Anahtar Kelimeler
Magnetoimpedance, Nanowire
Kaynak
Journal of Alloys and Compounds
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
561