Contrasting effects of metal oxide dopants on the superconductivity of YBa2Cu3O7-? ceramics
Küçük Resim Yok
Tarih
2019
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Bulk superconductor samples of YBa2Cu3O7-delta (YBCO or Y-123), with additions of 0.15 wt% MoO3, TiO2, RuO2 and two different types of Al2O3 compounds, are synthesized by a solid state reaction route. Structural, magnetic and transport properties of the samples are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), magnetic (M-H, M-T) and magneto-resistivity (MR-T) measurements. SEM investigations show that the addition of the Al2O3 obtained from the alumina crucible (Al2O3-cru) decreases the grain size of the sample which, in turn, degrades the transition temperatures (T-c) and magnetic critical current densities (Jcmag). On the contrary, the addition of the other metal oxides enhances of the samples by a few times and also increases T-c by up to 3 K. EDX analyses of the samples exhibit homogeneous distribution of additions, except for Ru-heterogeneities located around superconducting Y-123 grains. The highest J(c) and T-c values obtained on the RuO2 added sample were attributed to the agglomeration of the Ru-particles, which led to the optimal porosity that supports oxygenation process and intergrain coupling of the structure. From the DC magnetization data, we estimated Jcmagf 3.1 x 10(5) A/cm(2), 2.3 x 10(5) A/cm(2), 2 x 10(5) A/cm(2), 1.5 x 10(5) A/cm(2), 10(5) A/cm(2) and 5.1 x 10(4) A/cm(2) for the RuO2, TiO2, MoO3, Al2O3, undoped and Al2O3-cru added samples at 5 K under 0.25 T, respectively.
Açıklama
Anahtar Kelimeler
Magnetic-Properties, Ybco Films, Substitution, Irradiation, Transport, System
Kaynak
Journal of Materials Science-Materials in Electronics
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
30
Sayı
22