Fabrication of (BiGaPb)2Sr2Ca2Ca2Cu3O10+y glass-ceramic superconductor rods.
Küçük Resim Yok
Tarih
1996
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Plenum Publ Corp
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Glass samples with a nominal composition of B1.2Ga0.4Pb0.4Sr2Ca2Cu3O10+y were prepared as rods having a diameter of 13mm and 20cm long by melt casting technique. Sintering process was performed by applying a direct current to the glass rods. Three different current application stages were used and crystallisation of the glass rods were obtained. The XRD studies of the material showed that crystallised grains were preferably c-axis oriented. The best T-c was obtained at 107K and T-zero was obtained at 101K. These results were also confirmed by the D.C. Susceptibility measurements. After the optimum processing condition the maximum transport current density was found to be 9700 A/cm(2) at 4.2K.
Açıklama
International Conference on Physics and Chemistry of Molecular and Oxide Superconductors -- AUG 02-06, 1996 -- KARLSRUHE, GERMANY
Anahtar Kelimeler
Fibers
Kaynak
Journal of Low Temperature Physics
WoS Q Değeri
N/A
Scopus Q Değeri
N/A
Cilt
105
Sayı
5-6