Hydrogen effect on the field dependence of Young's modulus of FeCuNbSiB alloy
Küçük Resim Yok
Tarih
2002
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Sa
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The magnitude of the magnetic field dependence of Young's modulus of FeCuNbSiB alloys was found to decrease after hydrogenation but to nearly recover after 2-3 h. A large variation in the magnetic and the magnetoelastic properties of as-received sample was observed after hydrogenation. DeltaE and M-H results of samples annealed at 450degreesC showed that annealing could reduce hydrogen permeation into the sample. Practically no variation in the magnetic and magnetoelastic properties of samples annealed at 550degreesC were observed before and after hydrogenation. (C) 2002 Elsevier Science B.V. All rights reserved.
Açıklama
Anahtar Kelimeler
transition metal compounds, amorphous materials, gas-solid reaction, magnetization measurements
Kaynak
Journal of Alloys and Compounds
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
343
Sayı
1-2