Mechanical properties of high strength concrete made with pyrophyllite aggregates exposed to high temperature
Küçük Resim Yok
Tarih
2020
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Ernst & Sohn
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This paper presents the results of an experimental research on the assessment of the residual mechanical properties of high strength concretes (HSCs) made with pyrophyllite aggregate (PA) after high temperature. In the study, HSC mixtures with varying PA ratios (0, 25, 50, 75, and 100%) were subjected to elevated temperature (150, 300, 450, 600, and 750 degrees C) and then cooled in two different cooling regimes (air and water-cooling). The properties examined included compressive strength, weight loss, effects of cooling regime, and microstructure of HSC. The results of the study show that the increase in the PA ratios leads to a decrease in the compressive strength values. The results showed that weight loss of the specimens decreased with increasing PA ratios. It was found that the compressive strength values of HSC with PA cooled in air-cooling are higher than that cooled in water. When the compressive strength loss and the weight loss values are taken into consideration according to the control samples, the group with the highest resistance to high temperature (750 degrees C) effect was 100% PA group. Also, the internal structures of the samples exposed to high temperature were examined using scanning electron microscope and visual observations.
Açıklama
Anahtar Kelimeler
compressive strength, cooling regime, high strength concrete, high temperature, pyrophyllite aggregate, weight loss
Kaynak
Structural Concrete
WoS Q Değeri
Q2
Scopus Q Değeri
Q1