Jc enhancement and flux pinning of Se substituted YBCO compound
Küçük Resim Yok
Tarih
2013
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Y-2/3 Se1/3Ba2Cu3Ox compound was fabricated by using solid state fabrication technique. Optimum heat treatments conditions for Y0.77Se0.33Ba2Cu3Ox were investigated. It was determined that the XRD results of these samples were similar to Y-123 phase with some impurities. Magnetization dependence of applied magnetic fields was measured in the range of 0-9 T at 10-50 K. The symmetric and asymmetric M-H loops were obtained for the samples. Magnetization loops obtained from measurements were successfully described by the extended Valkov-Khrustalev model. The temperature and applied magnetic field dependencies of magnetization of sample were estimated and critical current density of samples was calculated by Bean model and pinning force of samples was calculated by using Lorentz force. It is found from critical current density values that Se additions were acted as a pinning center which increased critical current density.
Açıklama
Anahtar Kelimeler
Thin-Films, Yba2cu3o7-Delta, Magnetization, Superconductors, Crystals
Kaynak
Journal of Materials Science-Materials in Electronics
WoS Q Değeri
Q1
Scopus Q Değeri
Q2
Cilt
24
Sayı
12