Annealing effect on Magneto-impedance in CoSiB wires
Yükleniyor...
Dosyalar
Tarih
2020
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
In this study, thermal treatments dependence of Magneto-impedance (MI) effect in Co72.5Si12.5B15 wires has been investigated. Wires were annealed at 460 °C for different times (1- 400 min). It was found that low time annealed leads to increase in magnetic softness. The largest change in the MI was observed at 1 MHz frequency value. It was determined that maximum MI, coercivity (Hc) and maximum field sensitivity (S) values were 247%, 1.28 A/m and 1.35% per A/m respectively in the wire annealed at 460 °C for 10 minutes. This high MI and field sensitivity value occurring in low annealed time shows that this wire can be used in the design of low magnetic field sensors.
Açıklama
Anahtar Kelimeler
Kaynak
Adıyaman Üniversitesi Fen Bilimleri Dergisi
WoS Q Değeri
Scopus Q Değeri
N/A
Cilt
10
Sayı
2
Künye
BAYRİ N, ATALAY S, KOLAT V, İZGİ T, PEKTAŞ M (2020). Annealing effect on Magneto-impedance in CoSiB wires. Adıyaman Üniversitesi Fen Bilimleri Dergisi, 10(2), 620 - 629. 10.37094/adyujsci.740976