Comparison of Hashin and Puck criterions for failure behavior of pin loaded composite plates
Küçük Resim Yok
Tarih
2024
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
John Wiley and Sons Inc
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, the failure behavior of carbon fiber-reinforced pin-jointed composite plates were analyzed for different criteria. For this purpose, composite plates with a single and double pin joints were prepared from four layers carbon fiber composites. The effect of pin number, pin position on plate damage load and type was investigated experimentally and numerically under the tensile test. Numerically, progressive damage analysis was performed using Hashin and Puck failure criteria, and the approach rates to the experimental results were determined. It was observed that the experimental results obtained for single pin joint composites and the numerical data obtained using the Puck damage criterion were at least 87 % compatible, and this rate was determined as 85 % for the Hashin failure criterion. For the double pin jointed composites, it was seen that the experimental results and the results of the Puck damage criterion were compatible with at least 90 %, and this rate was obtained as 84 % for the Hashin failure criterion. The dominant damage type seen in the specimen is matrix shear and fiber compression according to the Hashin damage criterion, inter fiber failure in transverse tension for Puck. © 2024 Wiley-VCH GmbH.
Açıklama
Anahtar Kelimeler
hashin, laminated composite, pin joint, progressive failure analysis, Puck
Kaynak
Materialwissenschaft und Werkstofftechnik
WoS Q Değeri
Scopus Q Değeri
Q3
Cilt
55
Sayı
3