Fabrication of (BiGaPb)2Sr2Ca2Cu3O10+y glass-ceramic superconductor rods

Basit Öğe Kaydı
dc.authorscopusid7801562586
dc.contributor.authorYakqqncqq M.Eyyuphan
dc.date.accessioned2024-08-04T19:59:08Z
dc.date.available2024-08-04T19:59:08Z
dc.date.issued1996
dc.departmentİnönü Üniversitesien_US
dc.descriptionProceedings of the 1996 International Conference on Physics and Chemistry of Molecular and Oxide Superconductors, MOS'96 -- 2 August 1996 through 6 August 1996 -- Karlsruhe, Ger -- 45850en_US
dc.description.abstractGlass samples with a nominal composition of Bi1.2Ga0.4Pb0.4Sr2Ca2Cu3O10+y were prepared as rods having a diameter of 13 mm and 20 cm long by melt casting technique. Sintering process was performed by applying a direct current to the glass rods. Three different current application stages were used and crystallization of the glass rods were obtained. The XRD studies of the material showed that crystallized grains were preferably c-axis oriented. The best Tc was obtained at 107 K and Tzero was obtained at 101 K. These results were also confirmed by the D.C. Susceptibility measurements. After the optimum processing condition the maximum transport current density was found to be 9700 A/cm2 at 4.2 K.en_US
dc.identifier.endpage1540en_US
dc.identifier.issn0022-2291
dc.identifier.issue5 -6 pt 2en_US
dc.identifier.scopus2-s2.0-0030414906en_US
dc.identifier.scopusqualityQ2en_US
dc.identifier.startpage1535en_US
dc.identifier.urihttps://hdl.handle.net/11616/90421
dc.identifier.volume105en_US
dc.indekslendigikaynakScopusen_US
dc.language.isoenen_US
dc.publisherPlenum Publ Corp, New York, NY, United Statesen_US
dc.relation.ispartofJournal of low temperature physicsen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectBismuth compoundsen_US
dc.subjectCeramic materialsen_US
dc.subjectCritical current density (superconductivity)en_US
dc.subjectCrystallizationen_US
dc.subjectGlassen_US
dc.subjectMagnetic permeability measurementen_US
dc.subjectOxide superconductorsen_US
dc.subjectSinteringen_US
dc.subjectX ray diffraction analysisen_US
dc.subjectBismuth gallium lead strontium calcium copper oxideen_US
dc.subjectGlass rodsen_US
dc.subjectMaximum transport current densityen_US
dc.subjectMelt casting techniqueen_US
dc.subjectHigh temperature superconductorsen_US
dc.titleFabrication of (BiGaPb)2Sr2Ca2Cu3O10+y glass-ceramic superconductor rodsen_US